Sendust Powder core

  • Sendust Ring Inductors Powder Core

    Sendust Ring Inductors Powder Core

    Sendust Core, which is made from 6%Al,9%Si and 85%Fe,is mainly used to replace iron powder core because its core loss is 80% less than powdered iron, so it can be applied with the frequency above 8kHz.Sendust core has a saturation flux density of 1.05T and permeability from 14 to 125.The nearly zero magnetostriction alloy makes sendust ideal for eliminating audible frequency noise. Sendust core also has better DC bias characteristics and the best cost performance. It is mainly applied in AC inductor, output inductor ,in-line filter, power factor correction inductor etc. It can also be used as transformer core in some circumstances.

  • High Flux Cores

    High Flux Cores

    High flux iron nickel magnetic core is a kind of magnetic particle core containing 50% nickel and 50% iron with distributed air gap. HF iron nickel powder core has a saturation magnetic flux density of 13000 Gauss, and its loss value is much lower than that of pure iron powder core. It is an ideal choice for switching power modulation inductors, line noise filters, pulse transformers and flyback transformers. Especially in the case of large DC current, the use of HF magnetic powder core can effectively reduce the size of inductor, thereby reducing the total cost.

  • Sendust Core for Power Inductor

    Sendust Core for Power Inductor

    Iron silicon aluminum magnetic core, material composition: 85% iron, 6% aluminum, 9% silicon; Permeability from 26 to 125;It is mainly used in power inductors, AC inductors, output inductors, line filters, power factor correction circuits and other switching power supplies, sometimes replacing air gap ferrite as transformer core.

  • Sendust Cutting Core for Flat Wire Winding

    Sendust Cutting Core for Flat Wire Winding

    Although ferrosilicon has a higher saturation flux density, ferrosilicon has more advantages, such as better soft saturation, low core loss, temperature stability and lower cost. When the inductor uses the iron-silicon-aluminum magnetic powder core, the disadvantageous factors brought by the use of the air-gap ferrite magnetic ring can be eliminated.

  • Sendust Core Powder Inductor for AC Transformer

    Sendust Core Powder Inductor for AC Transformer

    Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000), low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T

  • High Inductance Sendust Core Sendust Block Core High Permeability

    High Inductance Sendust Core Sendust Block Core High Permeability

    Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000), low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T

  • Low loss Sendust Core for AC inductors

    Low loss Sendust Core for AC inductors

    Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000), low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T